· Next, θ'-precipitates nucleate at dislocations in the aluminum matrix. These zones grow by diffusion of copper from the θ'' zones, have edges that are incoherent with the matrix and, therefore, produce a reduced matrix strain field (d).

From: Ashby & Jones, "Engineering Materials 2," Pergamon (1986)